MONEL K500 is a age-hardenable Nickel-Copper alloy which combines the corrosion resistance of Alloy 400 with high strength corrosion fatigue and erosion resistance.
MONEL K500 is a nickel-copper alloy, precipitation hardenable through additions of aluminum and titanium. MONEL K500 retains the excellent corrosion resistant characteristics of 400 and has enhanced strength and hardness after precipitation hardening when compared with 400. Alloy K500 has approximately three (3) times the yield strength and double the tensile strength when compared with 400. MONEL K500 can be further strengthened by cold working before the precipitation hardening.
Characteristics
- Excellent mechanical properties from sub-zero temperatures up to about 480C.
- Corrosion resistance in an extensive range of marine and chemical environments. From pure water to non-oxidising mineral acids, salts and alkalis.
Applications
- Propeller and pump shafts.
- Pumps and valves used in the manufacture of perchlorethylene, chlorinated plastics.
Typical application for MONEL K500 which takes advantage of high strength and corrosion resistance are pump shafts, impellers, propeller shafts, valve components for ships and offshore drilling towers, bolting, oil well drill collars and instrumentation components for oil and gas production. It is particularly well suited for centrifugal pumps in the marine industry because of its high strength and low corrosion rates in high-velocity seawater.
MONEL K500 is non-magnetic. MONEL K500 should be annealed when welded and the weldment then stress relieved before aging.
High Performance Alloys, Inc. stocks Alloy K500 in a range of sizes including 3/8"-2-1/2" diameter cold drawn, annealed and aged, and 2-3/4"-10" diameter hot finished and aged. Material can be supplied in random lengths, cut to order or machined to your specifications. Machining includes drilling, turning, tapping, threading, CNC shapes, flanges and more.
Chemistry
| | Ni | Mn | Si | Fe | Al | S | C |
| Max | | 1.50 | 0.50 | 2.00 | 3.15 | 0.010 | 0.18 |
| Min | 63.00 | | | | 2.30 | | |
Tensile Data
| | Ultimate Tensile | Yield Strength (0.2% OS) | Elong. | Hardness Rockwell C, Min. | Hardness Brinell 3000 kg, min. |
| Cold Worked/SR Over 1(25.4) to 3 |
| Min | 140 KSi | 100 KSi | 17.0 | 29 | 280 |
| Max | | | | | |
| Min | 965 MPa | 690 MPa | | | |
| Max | | | | | |
| Hot Worked/ Aged Hardened |
| Min | 140 KSi | 100 KSi | 20.0 | 27 | 265 |
| Max | | | | | |
| Min | 965 MPa | 690 MPa | | | |
| Max | | | | | |
Specifications
| Form | Standard |
| Metal Type | UNS N05500 |
| Bar | ASTM B865 QQ-N-286 |
| Wire | AMS4676 |
| Sheet | ASTM B865 QQ-N-286 |
| Plate | ASTM B865 QQ-N-286 |
| Fitting | |
| Forging | QQ-N-286 Din 17754 |
| Weld Wire | FM 60 ERNiCu-7 |
| Weld Electrode | FM 190 ENiCu-7 Din 17753 |
| Din | 2.4375 |
Machining
Nickel & cobalt base corrosion, temperature and wear-resistant alloys, such as MONEL K500, are classified as moderate to difficult when machining, however, it should be emphasized that these alloys can be machined using conventional production methods at satisfactory rates. During machining these alloys work harden rapidly, generate high heat during cutting, weld to the cutting tool surface and offer high resistance to metal removal because of their high shear strengths. The following are key points which should be considered during machining operations:
CAPACITY - Machine should be rigid and overpowered as much as possible.
RIGIDITY - Work piece and tool should be held rigid. Minimize tool overhang.
TOOL SHARPNESS - Make sure tools are sharp at all times. Change to sharpened tools at regular intervals rather than out of necessity. A 0.015 inch wear land is considered a dull tool.
TOOLS - Use positive rake angle tools for most machining operations. Negative rake angle tools can be considered for intermittent cuts and heavy stock removal. Carbide-tipped tools are suggested for most applications. High speed tools can be used, with lower production rates, and are often recommended for intermittent cuts.
POSITIVE CUTS - Use heavy, constant, feeds to maintain positive cutting action. If feed slows and the tool dwells in the cut, work hardening occurs, tool life deteriorates and close tolerances are impossible.
LUBRICATION - lubricants are desirable, soluble oils are recommended especially when using carbide tooling.